Crusher Hammer Heads

Carbide Hammer

high manganese ｉｎｓｅｒｔ titanium alloy bars and hardfacing

Ceramic Composite Matrix Reinforcement

high manganese steel ｉｎｓｅｒｔ alloy bars

Metal Crusher Hammer

Crusher Hammer

Stone Crusher Hammer

Coal Crusher Hammer

Clinker Crusher Hammer

Crusher Hammer

High Manganese Steel Hammer

Clinker Crusher Hammer

We can provide you with various brands of Crusher Hammer Heads , also can customize and produce according to your working conditions

We can produce all kinds of crusher hammer heads, Including stone crusher hammer, coal crusher hammer, rock crusher hammer,chrome hammer, metal crusher hammer,limestone hammer, clinker crusher hammer, compo cast hammer, manganese steel hammer, Hammers With TiC Inserts,cast hammer etc. If you don't find the product you need on the website, please email us（info@lyzhili.com）, because we are a customized factory for crusher spare parts.

we can provides comprehensive material selection for you

High manganese steel(Mn13Cr2/Mn18Cr2), high manganese steel ｉｎｓｅｒｔ titanium alloy bars, high manganese ｉｎｓｅｒｔ titanium alloy bars and hardfacing, bimetal composite, medium alloy steel,high chromium cast iron, alloy steel,Ceramic Composite Matrix Reinforcement,Ceramic composite, etc.

Ceramic Composite Matrix Reinforcement

Our company's newly developed ceramic composite matrix reinforced hammer head incorporates cermet into a traditional high-manganese steel matrix, forming a multi-level composite material through in-situ self-generation technology. This hammer exhibits twice the hardness of Mn18Cr2 at room temperature, and its hardness decreases only slightly at high temperatures compared to room temperature, thus solving the problem of significant attenuation of wear resistance in high-manganese steel with increasing temperature.

High chromium iron

Feature:

We use proper alloying and and related technological measures to make the crusher hammer heads’ surface hardness reaches more than 58HRC , during the process of wearing will maintain high hardness and high wear resistance.

Technology process

The working part of hammer head we use the technique of directional solidification to make Cr7C3 type carbide is perpendicular to the part.The macro-hardness and micro hardness of carbide can be improved without reducing thoghness.

Application

Suitable for making wearable spare parts with lower impact load and simpler shape.

Chemical component

Grade	Chemical component%
Grade	C	Si	Mn	Cr	Mo	Ni	Cu	S	P
BTMCr15	2.0~3.3	≤1.2	≤2.0	14~18	≤3.0	≤2.5	≤1.2	≤0.06	≤0.10
BTMCr20	2.0~3.3	≤1.2	≤2.0	18~23	≤3.0	≤2.5	≤1.2	≤0.06	≤0.10
BTMCr26	2.0~3.3	≤1.2	≤2.0	23~30	≤3.0	≤2.5	≤2.0	≤0.06	≤0.10
1：Allowed to add microscale V,Ti,Nb,B and Re etc. 2：We will choose grade and specific component according to blow bars’ weight ,thickness and sizes

Mechanical Property

Grade	Surface Hardness
	Casting condition		Harded condition		Softening annealing condition
	HRC	HB	HRC	HB	HRC	HB
BTMCr15	≥46	≥450	≥58	≥650	≥41	400
BTMCr20	≥46	≥450	≥58	≥650	≥41	400
BTMCr26	≥46	≥450	≥58	≥650	≥41	400
1：There are no exact corresponing value between rockwell hardness(HRC) and brine hardness(HB),so ,this two kind of hardness value can be inspend used 。 2：The hardness in the 40%deepness of casting section should be lower than 92% hardness of surface.

Bimetal compisite material

Feature:

This material adopt special technological process to make two material with different property integrate in the same time when they are liquid state.

The bonded area could reach 100% and the impact toughness of the bonded area can get more than 14J/cm2 ,the working part use high Cr casting iron and adopt directional solidification to make Cr7C3 which included in high Cr casting iron perpendicular distribute to the working surface .

The hardness could reach to HRC62-65,and the impact to toughness(AK) is above 30J/cm2 ,It can resist the cutting from AL2O3 and SiO2 perfectly show the high anti-friction property . the hammer handle with high toughness and perfect combined mechanical properties.the material have both high anti-friction and safety property and solve the contradiction between the hardness and toughness effectively ,make the spare parts fit the wicked working condition.

The lifetime of the hammer which made from bimetal composite material is 2-3 times than the lifetime of normal high Mn hammer .Specially suit for the big crusher hammer ,blow bar and liner of big mill .The effect will be prominent in the wicked condition .It is widely used in limestone ,cementclinker,iron,sandstone,gangue ,basalt and so on.

Chemical component

Grade	Chemical component%
Grade	C	Si	Mn	Cr	Mo	Ni	S	P
ZG38CrMnSiMoNiRe	0.35~0.45	0.4~0.8	0.4~1.0	0.5~2.0	0.20~0.80	0.3~2.0	≤0.004	≤0.004

Mechanical Property

Grade	HRC Surface Hardness HRC	Shock absorption energy KN2/J（unnotched）
ZG38CrMnSiMoNiRe	50	25

High Manganese Steel

Feature

High manganese steel refers to high alloy steels containing more than 10% manganese. The biggest features of high-manganese steel are:

The greater external compressive stress or impact load, the more conducive to the formation of hardened layer, so the higher the wear resistance of the casting;

With the gradual wear of the hardened layer, new work hardened layers will continue to form under the influence of external compressive stress or impact loads. Therefore, it is suitable for making wearable spare parts that are subject to high impact load and wear for a long time, and is widely used in metallurgy, mining, building materials, railways, electric power, coal and other broken grinding equipment.

Chemical component

Grade	Chemical component%
Grade	C	Si	Mn	Cr	S	P
ZG120Mn13	1.05~1.35	0.3~0.9	11~14	-	≤0.06	≤0.04
ZG120Mn13Cr2	1.05~1.35	0.3~0.9	11~14	1.5~2.5	≤0.06	≤0.04
ZG120Mn17Cr2	1.05~1.35	0.3~0.9	16~19	1.5~2.5	≤0.06	≤0.04
1：Allowed to add microscale V,Ti,B and Re etc. 2：We can produce the other grade high manganese steel hammer according to customers’ requirments 。

Mechanical Property

Grade	Stretch property				Hardness HB
Grade	yield strength ReH/Mpa	tensile strength Rm/Mpa	Elongation at cross section %	Shock absorption energyKu2J	Hardness HB
ZG120Mn13	-	≥685	≥25	≥118	≤300
ZG120Mn13Cr2	≥390	≥735	≥20	-	≤300

Medium alloy steel

Feature

The alloy structure cast steel is an iron-carbon alloy formed by adding an appropriate amount of one or more alloy elements on the basis of ordinary carbon steel.

Process technology

According to the different elements added, with appropriate smelting and heat treatment process to obtain high strength, high toughness, high wear resistance, corrosion resistance, low temperature resistance, high temperature resistance, non-magnetic and other related special properties.

Scope of application

It is suitable for producing the wear-resisting spare parts with good mechanical strength and good toughness that are required for various working conditions, and the main steel structure castings with the required dynamic load.

Chemical component

Grade	Chemical component%
Grade	C	Si	Mn	Cr	Mo	S	P	Ai
ZG42CrMo	0.38-0.43	0.15-0.35	0.75-1.00	0.80-1.10	0.15-0.25	<0.04	<0.035	-
ZG35CrMo	0.32~0.40	0.17~0.37	0.40~0.70	0.80~1.10	0.15~0.25	≤0.035	≤0.035	-
ZG38CrMoAl	0.35~0.42	0.20~0.45	0.30~0.60	1.35~1.65	0.15~0.25	≤0.04	≤0.04	0.7~1.1
ZG40Cr	0.37~0.45	0.17~0.37	0.5~0.8	0.8~1.1	-	-	-	-
ZG30Mn2SiCrMo	0.25~0.35	0.40~0.80	1.20~1.60	1.35~1.65	0.2~0.5	≤0.04	≤0.04	-

Mechanical Property

Grade	tensile strength（Mpa）	yield strength （Mpa）	Elongation at cross section（%）	reduction of crosssection area（%）	Shock absorption energy（KV₂/J）
ZG42CrMo	≥1080	≥930	≥12	≥20	≥24
ZG35CrMo	≥985	≥835	≥12	≥20	≥24
ZG38CrMoAl	≥980	≥835	≥14	≥20	≥24
ZG40Cr	≥980	≥785	≥9	≥20	≥24
ZG30Mn2SiCrMo	≥1500	≥1300	≥3	-	≥24